| | BI9/0,8 | BI11/0,9 | BI11/1,1 | BI11/1,3 | BI12/1,3 | BI13/1,3 | BI14/1,3 | BI14/1,4 |
Method of application | | Cast | Gun | Cast | Gun | Cast | Gun | Cast | Gun | Cast | Gun | Cast | Gun | Cast | Gun | Cast | Gun |
Temperature of application, max. | ℃ | 900 | 900 | 1100 | 1100 | 1100 | 1100 | 1100 | 1100 | 1200 | 1200 | 1300 | 1300 | 1400 | 1400 | 1400 | 1400 |
Cold crushing strength after drying at 105 ℃, min. | MPa | 3.5 | 4.5 | 7.5 | 8.5 | 6 | 9 | 9 | 12 | 12 | 14 | 9 | 11 | 12 | 13 | 12 | 13 |
Cold crushing strength after firing at temperature of application, min | MPa | 2 | 2.7 | 4 | 4.5 | 3 | 3.5 | 7 | 9.5 | 7.5 | 8 | 3 | 4 | 4.5 | 5.5 | 4.5 | 5.5 |
Bulk density after firing at temperature limit of application, min | g/cm³ | 0.8 | 0.85 | 0.9 | 0.95 | 1.1 | 1.15 | 1.3 | 1.35 | 1.3 | 1.35 | 1.3 | 1.35 | 1.3 | 1.35 | 1.4 | 1.45 |
Thermal conductivity at 400 ℃ | W/mK | 0.16 | 0.17 | 0.23 | 0.25 | 0.3 | 0.31 | 0.34 | 0.35 | 0.32 | 0.33 | 0.4 | 0.41 | 0.42 | 0.43 | 0.42 | 0.43 |
Thermal conductivity at 600 ℃ | W/mK | 0.2 | 0.22 | 0.26 | 0.28 | 0.34 | 0.35 | 0.39 | 0.4 | 0.35 | 0.36 | | | | | | | | |
Thermal conductivity at 800 ℃ | W/mK | 0.24 | 0.26 | 0.31 | 0.33 | 0.36 | 0.37 | 0.43 | 0.45 | 0.4 | 0.42 | | | | | | | | |
Thermal conductivity at 1000 ℃ | W/mK | | | 0.33 | 0.35 | 0.41 | 0.43 | 0.46 | 0.48 | 0.52 | 0.54 | 0.5 | 0.52 | 0.55 | 0.59 | 0.57 | 0.59 |